When should you use galvanized steel or zinc plated steel?

Both add a layer of zinc to the outside of the product. Zinc plating looks shiny and pretty, galvanized looks dull. But don’t be a magpie and just pick up the shiny object – think about the use.

Both methods add a protective layer of zinc to the steel.  Zinc protects the steel by sacrificing itself – called a “sacrificial anode”. When exposed to the atmosphere, the pure zinc (Zn) reacts with oxygen (O2) to form zinc oxide (ZnO), which further reacts with carbon dioxide (CO2) to form zinc carbonate (ZnCO3), a usually dull grey, fairly strong material that stops further corrosion in many circumstances, protecting the steel below from the elements. Zinc is also able to protect at a distance. All of the surface need not be covered with zinc. Ships attach large blocks of zinc to the hulls to protect the hull from corrosion. Ships need not cover the hull with zinc anodes. They are placed near and in electrical contact with the hull.

Hot-dip galvanizing results in a metallurgical bond between zinc and steel. It is the process of coating iron, steel, or aluminium with a thin zinc layer, by passing the metal through a molten bath of zinc at a temperature of around 860 °F (460 °C). The finished product can be used up to 200Oc (above that the zinc can peel)

Zinc plating is performed by cleaning the metal surface with an alkaline detergent, then treating with acid to remove exiting rust. Next, Zinc is deposited on the metal by immersing in a chemical bath containing dissolved zinc. A DC current is applied resulting in the Zinc being deposited on the product

So when to use Zinc Plating, and when to use hot dip galvanizing?. Well the shiny pretty one is Zinc plating, and the plating is only typically 3 microns thick, the dull one is galvanized and is typically 50 microns thick and therefore provides much more protection.
So actually the choice is quite simply, where you only need superficial protection, indoors in a dry climate (and want the aesthetic value) go for zinc plating. Outdoors, or a more wet climate use hot – dip galvanise

But wait there is a third method – and one to be wary of. Cold galvanizing is really painting with a zinc rich primer. Although this does offer some protection – a protective layer – against rusting, as soon as it is scratched, moisture can get at the underlying steel and therefore cause rust and corrosion.  Always ask your supplier if they supply hot dip galvanizing – because only that is true galvanising

Graphskill use a refined version of Hot-dip galvanising on all their products. The process is called Hot – Spin Galvanising. Material is immersed in molten zinc at a temperature of around 450 degrees until the temperature of the work is the same as the Zinc. During this process the molten zinc reacts with the surface of the steel to form a series of zinc/iron alloys. These alloy layers protect steel from corrosion for 30-40 years and more. Work is rapidly removed from the zinc, before the zinc on its surface solidifies, the basket is placed in a centrifuge and spun for several seconds. This removes excess zinc from the surface and prevents the items sticking together to ensure a smooth finish. Work is then transferred to a quench tank where it is cooled to allow handling.

Hot-spin galvanising is particularly useful for Threaded fasteners. For ISO metric fasteners the galvanising build up on the thread of one component requires an extra clearance of four times the coating thickness to enable assembly into the mating component. Normal practice would be to galvanise standard tolerance bolts, mating nuts are galvanised as blanks then tapped 0.4 mm oversize with the tread lightly oiled. When assembled the but thread is protected by direct contact with the galvanised coating on the bolt.

The UK galvanizers association website: http://www.galvanizing.org.uk/index.php